乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129 乐泰 3129/乐泰3129/环氧胶3129
乐泰 3129
技术服务热线：021-51693135
TYPICAL CURING PERFORMANCE
Recommended Curing Conditions
5 to 10 minutes @ 80 °C
Note: With all fast cure systems, the time required for cure depends
on the rate of heating. Conditions where a hot plate or heat sink is
used are optimum for fastest cure. Cure rates depend on the mass of
material to be heated and intimate contact with the heat source. Use
suggested cure conditions as general guidelines. Other cure
conditions may yield satisfactory results.
TYPICAL PROPERTIES OF CURED MATERIAL
Cured for 30 minutes @ 80 °C
Physical Properties:
Coefficient of Thermal Expansion,
ISO 11359-2, K-1:
Physical Properties:
Coefficient of Thermal Expansion,
ISO 11359-2, K-1:
alpha 1 47
alpha 2 145
Glass Transition Temperature, °C:
(Tg) via DMA 35
Storage Modulus, @ 25°C by DMA GPa 5.4
(psi) (780,000)
Tensile Modulus MPa 200
(psi) (29,000)
Tensile Strength MPa 36.4
(psi) (5,300)
TYPICAL PERFORMANCE OF CURED MATERIAL
Adhesive Properties
Cured for 30 minutes @ 80 °C
Lap Shear Strength, ISO 4587:
Epoxyglass N/mm2 15.4
(psi) (2,230 |